Elastollan® SP 9322
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MdLv4c_Elastollan-SP-9322.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyester-Polyurethane Compound with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristic and high resilience performance, phthalatfree. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 52 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 120 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 0.700 | MPa | DIN 53504-S2 |
| 100% strain | 1.80 | MPa | DIN 53504-S2 |
| 300% strain | 4.60 | MPa | DIN 53504-S2 |
| Tensile Strength | 25.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 900 | % | DIN 53504-S2 |
| Tear Strength 1 | 35 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | ISO 815 |
| 70°C, 24 hr | 38 | % | ISO 815 |
| 100°C, 24 hr | 53 | % | ISO 815 |
| Additional Information |
|---|
| The plaques are manufactured by injection moulding from pre-dried granules (water content less 0,02%). Test paques are aged 20 hrs at 100°C.Specimens are cut from test plaques. The test conditions: 23°C ± 2°C and 50% ± 6% rel. humidity. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 185 - 210 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C | |
| Injection Rate | Slow |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XENOY™ 1102 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| EVALENE® HDPE HM10561 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| DOMAMID® 66G35V0P 1001 A | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| HiFill® POM CO 0374 S | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Hylon® N1000MDL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |