GETILAN ATP/190 X 1S
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MW9Lg0_GETILAN-ATP-190-X-1S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN ATP/190 is a high density chemically crosslinkable polythene to produce insulation and sheathing of electrical cables. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our type MAC/202. REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.50 - 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 390 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ISO 306 |
| Service Temperature | -60 - 100 | °C | |
| Thermoset 1 | |||
| 200°C | 40 | % | IEC 60811 |
| Residual | -5.0 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Cylinder Zone 5 Temp. | 205 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90 °C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayflex® WR-80 | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| CP PRYME® Nylon 66 NN213HSL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Escorene™ Ultra FL 00218 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| ISPLEN® PB 130 G1M | REPSOL | PP Impact Copolymer | ISPLEN® |
| omay® SC42 | Suzhou OMAY Optical Materials Co., Ltd | Film, PP | omay® |