REPRO PP RT314
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Rondo Plast AB |
| Trademark: | REPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MDHzgA_REPRO-PP-RT314.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20% talcum reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow | 0.90 to 1.2 | % | |
| Flow | 0.90 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 1800 | MPa | ISO 178 |
| Flexural Stress | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 40.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9266-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Calprene® 412 | Dynasol Elastomers | SBS | Calprene® |
| Infino XP-2165BM | SAMSUNG SDI CO., LTD. | PPS | Infino |
| Karina IVORY PVC COMPOUND 90900-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TOTAL Polypropylene PPH 3485WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |