HiFill FR® PC 1003 UV is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 140 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 320 | J/m | |
| 23°C, 3.18 mm | 850 | J/m | |
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 430 | J/m | |
| 23°C, 6.35 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 132 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 266 to 293 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® B3 N | Nilit Plastics | Nylon 6 | NILAMID® |
| Aristech Acrysteel® IMA | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| DURACON® HP270X | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| EPO-TEK® H65-175MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ LUBRICOMP™ RFL16 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |