TEKALOY™ G70A2
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M45FIV_TEKALOY-G70A2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKALOY™ G70A2 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 55.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 2160 | MPa | ASTM D790 |
| Flexural Strength | 82.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 113 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENITER 0037 | Vamp Tech | PBT | DENITER |
| ELASTOSIL® R 780/80 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Hostacom G4 R01 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Hytrel® 3078FG | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina RED COLOR CONCENTRATE 42/ 50-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |