MAJORIS BT410
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M39h6f_MAJORIS-BT410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BT410 is a 40% mineral filled polypropylene compound intended for injection moulding. The light natural colour of BT410 makes it easy to reach any colour tone. The compound is also supplied ready coloured according to the customer' requirements. BT410 is intended for components which require good long-term heat resistance, very high heat distortion temperature, excellent rigidity, low shrinkage and high dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 21 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A |
| -- | 108 | °C | ISO 306/B |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Stability (150°C) | > 700.0 | hr |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayflex® 180 RRIM (20% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| EnviroPro 1020GF30 | West Michigan Compounding | PP Copolymer | EnviroPro |
| LEXAN™ LC120 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| EPAMOULD 665A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| Sylvin 9779-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |