Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | National Petrochemical Industries Company (NATPET) |
Trademark: | Teldene® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | LrSHga_TeldeneH08CFM.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Typical Applications
Key Characteristics
|
General Information | |
---|---|
Features |
|
Uses |
|
Appearance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density (23°C) | 0.900 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield | 34.0 | MPa | ISO 527-2/50 |
Fracture | 23.0 | MPa | ISO 527-2/50 |
Tensile Strain | ISO 527-2/50 | ||
Yield | 13 | % | ISO 527-2/50 |
Fracture | 650 | % | ISO 527-2/50 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 4.6 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
Vicat Softening Temperature | 154 | °C | ISO 306/A50 |
Optical | Nominal Value | Unit | Test Method |
---|---|---|---|
Gloss (45°, 100 µm) | 88 | ASTM D2457 | |
Haze (100 µm) | < 1.0 | % | ASTM D1003 |
Extrusion | Nominal Value | Unit | |
---|---|---|---|
Melt Temperature | 240 - 260 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sinpolene MBB2801 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
TUFNYL® RGF 33 NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
Fenochem C 3500 | Chemiplastica, Inc. | Phenolic | Fenochem |
Hapflex™ 673-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
Plaslube® NY-1/MS/5 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |