TECHNYL® A 218HPS V50 BLACK 21N
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® RED |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M2UmxX_TECHNYLA218HPSV50BLACK21N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218HPS V50 is a polyamide blend of polyamide 6.6 polyamide 6 reinforced with 50% of glass fiber, high heat stabilized for injection moulding. This grade is designed to offer a long term heat resistance and is suitable to work in environments characterized by a very high temperature. (210°C) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | ||
| -- | 0.25 | % | ISO 294-4 |
| Transverse flow | 0.61 | % | ISO 294-4 |
| Flow | 0.15 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 17800 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 239 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 2.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 366 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 98 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 254 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 239 | °C | ISO 75-2/Af |
| Melting Temperature | 248 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003S1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Hanwha Total PE 4220F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Pemex BDL 92020 S | Pemex Petroquímica | LLDPE | Pemex |
| POLYCOMPO PP V7400 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| Sylvin 8218-85 Yellow 4182 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |