Trexprene® A70CI
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgXCw0_Trexprene-A70CI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A70CI is a heat stabilized and UV Stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This pre-colored compound is for interior applications. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 to 0.990 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 70 to 78 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 2.80 | MPa | |
| Flow : 100% Strain | 3.60 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Break | 5.50 | MPa | |
| Flow : Break | 5.70 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 620 | % | |
| Flow : Break | 510 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 27 | kN/m | |
| Flow | 27 | kN/m | |
| Compression Set | |||
| 70°C, 24 hr | 33 | % | ASTM D395B |
| 70°C, 24 hr 5 | 33 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 1000 hr) | -1.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (110°C, 1000 hr) | -10 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -53.0 | °C | ASTM D746 |
| Type B | -53.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Fogging - Dry Fog | 86 | % | SAE J1756 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Fastness | |||
| to Burnt Gas, AATCC Rating : 60°C 6 | > 4.00 | ||
| to Burnt Gas, Change in Color : 60°C 7 | Delta E < 3 | ||
| to Burnt Gas, Yellowness Index : 60°C 8 | < 2.00 | YI | |
| to Light 9 | Delta E < 3 | ||
| Odor Rating 10 | > 7.00 | ||
| Ozone Resistance (40°C) 11 | 0 Rating | ISO 1431-1 | |
| Weatherability | |||
| Arizona 12 | Delta E < 3 | ||
| Florida 13 | Delta E < 3 | SAE J1976 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | ISO 105-G02, AATCC TM 23, 168 h |
| 7 . | ISO 105-G02, AATCC TM 23, 168 h |
| 8 . | ISO 105-G02, AATCC TM 23, 168 h |
| 9 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 10 . | GMW3205 Code B |
| 11 . | 100 pphm, Method A |
| 12 . | 105,000 TNR Langleys exposure per GMW3417 L1, F2, G1, T5 |
| 13 . | 2 years exposure, Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S210 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Unichem 93-636B | Colorite Polymers | PVC, Unspecified | Unichem |
| Aristech Solarcast® | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| Durethan® B 38 F KA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| Osterlene® HD-.04-948 | Osterman & Company | HDPE | Osterlene® |