AKROMID® B3 GF 30 S3 natural (2984)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LfWVkD_AKROMID-B3-GF-30-S3-natural-2984-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 S3 natural (2984) is a 30% glass fibre reinforced, dry impact resistant polyamide 6 with high stiffness and strength and light inherent color Applications are housings and covers for the automotive industry and power tools |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.33 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 52.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.30 | -- | % | |
| Flow | 0.80 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.4 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 5.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.5 | 12 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 16 | kJ/m² | |
| 23°C | 25 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | > 100 | > 100 | kJ/m² | |
| 23°C | > 100 | > 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R540 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Xuchuan A-8060/B-6018 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| NEXUS PE HDPE-00649 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| LNP™ LUBRICOMP™ DCL33E compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| Petrothene® GA502 | LyondellBasell Industries | LLDPE | Petrothene® |