PENTESTER BT L H schwarz
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTESTER BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yEfIaf_PENTESTER-BT-L-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyester PBT, slightly impact moidified, easy flowing |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 1.6 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 175 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 53.0 | MPa | ISO 527-2 |
| Fracture | 53.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.5 | % | ISO 527-2 |
| Fracture | 20 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.20 | IEC 60250 | |
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| ISO Description: PBT, MPRMC, 13-020The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >20% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 245 - 270 | °C | |
| Middle Temperature | 255 - 280 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 45.0 | MPa | |
| Holding Pressure | 24.8 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1185 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shanghai Potomer SG8 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Latishield 66-10A H2 CETG/400 | LATI S.p.A. | Nylon 66 | Latishield |
| Karina MBU BLUE -E 06/948-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® BKV 115 H2.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |