Starex VH-0815 M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LdsDev_StarexVH0815M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex VH-0815 M is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The application fields of Starex VH-0815 M include electrical/electronic applications and electrical appliances. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.31 - 0.59 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.31 - 0.59 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.31 - 0.59 | % | ISO 2577 |
| Traffic : 3.20mm | 0.31 - 0.59 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 105 | ASTM D785 | |
| R scale | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2270 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 40.5 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 31.5 | MPa | ASTM D638 |
| Fracture | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 15 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2180 | MPa | ASTM D790 |
| -- 6 | 3480 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 60.3 | MPa | ASTM D790 |
| -- 8 | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 210 | J/m | ASTM D256 |
| 23°C 10 | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 85.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 86.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 70.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.5 85.7 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm, Black | V-2 | UL 94 | |
| 1.5 mm | V-1 | UL 94 | |
| 2.0 mm | V-0 5VB | UL 94 | |
| 3.0 mm | V-0 5VA | UL 94 | |
| 2.5 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 50 - 70 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.981 - 2.45 | MPa | |
| Screw Speed | 40 - 50 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P885RSUA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Formolon® 38 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| ESPRENE EPDM 301A | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| OmniCarb™ PC/PET 325 | OMNI Plastics, LLC | PC+PET | OmniCarb™ |
| TechnoElast V A7000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |