Task® 4
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Task® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L8WVf1_Task-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TASK® 4 is a unique polyurethane casting resin that is very strong when cast in Ultra-Thin sections ranging from 0.03" to 0.50"(0.075cm to 1.27cm). TASK® 4 has a very low mixed viscosity, ensuring flawless pick-up of even the finest detail. Cured plastic exhibits very low shrinkage which is why this plastic has become a favorite of prototype and design professionals throughout the world. Pot life is 20 minutes and cure time is 16 hours at 73°F/23°C. Vibrant colors and color effects are possible by adding SO-Strong® color tints. Fully cured models made from TASK® 4 are tough, durable, machinable and paintable. They resist moisture and mild solvents. Applications for TASK® 4 include making prototype and architectural models, model toys, durable miniatures, ultra-thin mechanical parts and special effect props. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.863 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:100B by weight |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.35 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 896 | MPa | ASTM D638 |
| Tensile Strength (Break) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 1410 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Compressive Modulus | 517 | MPa | ASTM D695 |
| Compressive Strength | 51.0 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 43.3 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 20 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 250 | cP | ASTM D2393 |
| Demold Time 1(23°C) | 960 | min |
| Note Message | |
|---|---|
| 1 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPOA1090 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| VENELENE® FB-3030 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE+LLDPE | VENELENE® |
| Topilene® J740 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Color-in™ MA504-M | Shanghai KumhoSunny Plastics Co., Ltd. | Acrylic (PMMA) | Color-in™ |
| Globalene® ST302 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |