GELOY™ CR7520 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ku5tXW_GELOY-CR7520-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 7.0 | g/10 min | |
| 260°C/5.0 kg | 13 | g/10 min | |
| 280°C/3.8 kg | 20 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C) | 0.55 | % | ASTM D570 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1790 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 41.4 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Break 3 | 34.5 | MPa | ASTM D638 |
| Break | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 3.1 | % | ISO 527-2/50 |
| Break 4 | 40 | % | ASTM D638 |
| Break | 44 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 1790 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength 7(Yield, 50.0 mm Span) | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 59 | J/m | ASTM D256 |
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 9 | 4.5 | kJ/m² | ISO 180/1A |
| 23°C 10 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 20.0 | J | |
| 23°C, Total Energy | 35.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 87.8 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 90.6 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 91.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 76.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 79.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 80.0 | °C | ISO 75-2/Af |
| 1.8 MPa, Annealed | 95.6 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 99.4 | °C | ASTM D1525 13 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE | ASTM E831 | ||
| Flow : -30 to 0°C | 8.5E-5 | cm/cm/°C | |
| Flow : -40 to 40°C | 8.6E-5 | cm/cm/°C | |
| Flow : 0 to 100°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.2E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 5.20 | ||
| 60 Hz | 5.20 | ||
| 1 MHz | 3.21 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 0.15 | ||
| 60 Hz | 0.15 | ||
| 1 MHz | 0.026 | ||
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 95 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 221 to 249 | °C | |
| Middle Temperature | 227 to 260 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 238 to 271 | °C | |
| Processing (Melt) Temp | 238 to 271 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4700 TFE 10 | RTP Company | PTT | RTP |
| Tru-Bond™ PSA 3000 | Devcon | Acrylic, Unspecified | Tru-Bond™ |
| Xuye Z-500 | Shandong Xuye New Materials Co., Ltd. | CPVC | Xuye |
| NEFTEKHIM PP 1525H (S28F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Sylvin 7011EE-70 WHITE 1161 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |