EnCom ABS 5025
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UhPk5g_EnCom-ABS-5025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade Utility ABS |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 21 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 92.2 | °C | |
| 1.8 MPa, Unannealed | 87.8 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.57 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 7.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 188 to 232 | °C | |
| Middle Temperature | 204 to 246 | °C | |
| Front Temperature | 218 to 260 | °C | |
| Nozzle Temperature | 218 to 274 | °C | |
| Processing (Melt) Temp | 218 to 274 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.172 to 0.689 | MPa | |
| Screw Speed | 25 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TFE 20 | RTP Company | PPS | RTP |
| UNITIKA Nylon 66 B2040G33 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Axiall PVC 6850 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LNP™ THERMOCOMP™ JF006LXZ compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| LUVOCOM® 1105-8059 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |