Ravamid® AGF35 BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ravago Group |
| Trademark: | Ravamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KtDh1Z_Ravamid-AGF35-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Black, 35% glass fibre reinforced, general purpose All the products are also available Heat Stabilized (H) and UV Stabilized (UV) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 1.5 | % | ASTM D955 |
| Humidity | < 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ASTM D882, ISO 527-2 |
| Tensile Strength (Break) | 130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) (23°C) | 7.50 | kJ/m² | ASTM D256 |
| Notched Izod Impact Strength (23°C) | 7.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 230 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.20 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC 840 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| Borclear™ RC737MO | Borealis AG | PP Random Copolymer | Borclear™ |
| DynaMix Lite™ 3244-GB | Polymer Dynamix | PEEK | DynaMix Lite™ |
| Karina WHITE PVC COMP. -E 871-10/366-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| ALTECH® PA6 ECO 2010/506 GF10 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |