TABOREX TA 1117 HD

Category:	HDPE , High Density Polyethylene
Manufacturer:	SILON s.ro
Trademark:	TABOREX
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Koqrtl_TABOREX-TA-1117-HD.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
A chemically-crosslinkable HDPE compound for the production of multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. It is designed to achieve best performance in single layer and co-extrusion products. TABOREX TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes which are produced with the SILON grade TABOREX TA 1117 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product provides all the superior properties associated with crosslinked polyethylene.

Message

A chemically-crosslinkable HDPE compound for the production of multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. It is designed to achieve best performance in single layer and co-extrusion products.

TABOREX TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes which are produced with the SILON grade TABOREX TA 1117 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards.

This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product provides all the superior properties associated with crosslinked polyethylene.

General Information
Features	Crosslinkable
Uses	Piping system
Forms	Sphere
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.948	g/cm³	DIN 53479, ASTM D1505
Apparent Density	0.54	g/cm³	DIN 53466
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238, ISO 1133
Volatile Matter ¹		%	Internal method
Gel Content	70	%	EN 579

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	24.0	MPa	ISO 527-2
Tensile Strain (Break)	450	%	ISO 527-2

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 - 90.0	°C
Drying Time	2.0	hr
Cylinder Zone 1 Temp.	160 - 170	°C
Cylinder Zone 2 Temp.	170 - 180	°C
Cylinder Zone 3 Temp.	170 - 190	°C
Cylinder Zone 4 Temp.	170 - 190	°C
Die Temperature	190 - 220	°C

Extrusion instructions
L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C

Note Message
1 .	ITN-ZP 300CH 3-5-5/d

Resin Grade	Manufacturer	Category	Trademark
Smoothblend® POM-1200	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	Acetal (POM) Homopolymer	Smoothblend®
APEX® 84-G466A-5	Teknor Apex Company	PVC, Flexible	APEX®
DESOX™ DSC640G10	DESCO Co., Ltd.	PBT+PET	DESOX™
Evolue™-H SP7005	Prime Polymer Co., Ltd.	HDPE	Evolue™-H
Paryls® PPSU F1250	Youju New Materials Co., Ltd.	PPSU	Paryls®