LNP™ THERMOCOMP™ IF006 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1tH060_LNP-THERMOCOMP-IF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* IF006 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound IF-1006 Product reorder name: IF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.66 to 0.71 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 to 0.16 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9580 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 182 | MPa | ASTM D638 |
| Break | 178 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.7 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9310 | MPa | ASTM D790 |
| -- | 8830 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 291 | MPa | ASTM D790 |
| -- | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 78 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.0 | J | ASTM D3763 |
| -- | 3.04 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 214 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 198 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 26 T 20 FRD 1 | Plastcom | PP, Unspecified | SLOVALEN® |
| AMTOPP WT30 | Inteplast Group | PP, Unspecified | AMTOPP |
| ESPOLEX 903 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Kpren 130B | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| Karina IVORY PVC COMPOUND 750-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |