NOVALAC FM 9001
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | NOVALAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Knhrdg_NOVALAC-FM-9001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 9001 is a fiberglass and mineral reinforced phenolic molding compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 72.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 14500 | MPa | ASTM D790 |
| Flexural Strength (Break) | 130 | MPa | ASTM D790 |
| Compressive Strength | 275 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 38 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 190 | °C | ASTM D648 |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ASTM properties listed were tested in accordance with ASTM D5948.Powder Density, ASTM D1895: 0.8 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.15%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9455-80 Clear 876 | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| Zytel® 80G14AHS NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| ExxonMobil™ HDPE HD 6601.29 | ExxonMobil Chemical | HDPE Copolymer | ExxonMobil™ HDPE |
| INELEC PESCF30 | Infinity LTL Engineered Compounds | PESU | INELEC |
| Vyncolit® TX10916 | SBHPP | Phenolic | Vyncolit® |