INNOPOL® PP CS 1-1240
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KesvKf_INNOPOL-PP-CS-1-1240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-1240 is a 42 % chalk -filled polypropylene homopolymer compound /PP-H KD42 (ISO 1043)/. INNOPOL® CS 1-1240 is developed for producing injection moulded components for household equipments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Ash Content (900°C) | 24 | % | ISO 3451-1A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.7 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 119 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Hold pressure: 30 to 80 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VE VEEP 115 | Mitsubishi Chemical Performance Polymers, Inc. | PVC+NBR | tefanyl® VE |
| Wellamid® MR409 22H-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NEALID XG400 | AD majoris | Nylon+Olefin | NEALID |
| Di-Pak™ E-4501-5 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| SIBUR Synthetic Rubber IR SKI-3 NST Group II | SIBUR | IR | SIBUR Synthetic Rubber |