TYNE® ABS CBL 85
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Tyne Plastics LLC. |
| Trademark: | TYNE® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SS84xx_TYNE-ABS-CBL-85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Data was measured on natural colored test specimens. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.4 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 102 | °C | |
| 1.8 MPa, Annealed | 97.2 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA E450 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Shuman ABS/PC 330 | Shuman Plastics, Inc. | PC+ABS | Shuman ABS/PC |
| WanBlend® WHT-8185M | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| HiFill® ASA 814 GY | Techmer Engineered Solutions | ASA | HiFill® |
| Osterlene® LLDH-1-918 | Osterman & Company | LLDPE | Osterlene® |