K-Resin® SBC KR53
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | K-Resin® SBC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KSlGGk_K-Resin-SBC-KR53.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Resin® SBC KR53 is a Styrene Butadiene Block Copolymer (SBC) material. It is available in North America. Important attributes of K-Resin® SBC KR53 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 750 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 590 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 25.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 180 | % | |
| TD : Break, 25 µm, Blown Film | 180 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 580 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 20 | g | |
| TD : 25 µm, Blown Film | 25 | g | |
| Oxygen Permeability (25 µm, Blown Film) | 110 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 1.5 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (0.0254 mm, Blown Film) | 1.10 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.8 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (25.4 µm, Blown Film) | 140 | ASTM D523 | |
| Haze (25.4 µm, Blown Film) | 0.20 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP229R | LyondellBasell Industries | Polyolefin, Unspecified | Moplen |
| Vital-Line SHE5800 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| DINALON® A3S25 | Grupo Repol | Nylon 66 | DINALON® |
| GAPEX® RPP30EA23BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Karina CLEAR PVC COMPOUND -E 800/206-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |