ZEONOR® 1020R
| Category: | COP , Cyclo Olefin Polymer |
| Manufacturer: | Zeon Corporation |
| Trademark: | ZEONOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KQvLck_ZEONOR-1020R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZEONOR® is a new line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by ZEON CORPORATION using proprietary technology for a wide range of electronic, automotive and packaging applications. ZEONOR can easily be processed for any of these applications by injection molding, blow molding or extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 20 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress | 53.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 90 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 101 | °C | ASTM D648 |
| Glass Transition Temperature | 102 | °C | JIS K7121 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 92.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| DuPont Impact Strength | 36.0 | J |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2201 | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| CABELEC® CC6057 | Cabot Corporation | PP Copolymer | CABELEC® |
| KEBAFLEX® S 70 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| Petrotene® PP A3 T10 PRTA010 PH380 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Durethan® ECO BKV 20 FN20 000000 | LANXESS GmbH | Nylon 6 | Durethan® |