WELLAMID Nylon 6000/51 GV 30 HWCP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K1YW2X_WELLAMID-Nylon-6000-51-GV-30-HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6000/51 GV 30 HWCP is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Europe. Important attributes of WELLAMID Nylon 6000/51 GV 30 HWCP are:
Typical application of WELLAMID Nylon 6000/51 GV 30 HWCP: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 4.00 mm | 0.80 | -- | % | |
| Flow : 4.00 mm | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 to 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8500 | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | 7200 | -- | MPa | DIN 52457 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 32 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | 110 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Melting Temperature | 215 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 2.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.022 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6411-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NuSil CV3-1144-1 | NuSil Technology | Silicone | NuSil |
| ALFATER XL® D50E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Ecomass® 4703ZD95 | Ecomass Technologies | TPU, Unspecified | Ecomass® |
| LUVOCOM® 1105-7809/BK VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |