POLYCASA® ACRYL G 66

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Polycasa
Trademark:	POLYCASA® ACRYL
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ivp6pN_POLYCASA-ACRYL-G-66.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polycasa Acryl is the trade name for thermoplastic moulding compounds from Polycasa.

Polycasa Acryl is a highly transparent, amorphous thermoplastic based on polymethylmethacrylate (PMMA), whilst Polycasa Acryl KR products are high-impact modified products with a range of melt viscosities.

CHARACTERISTICS

Available in many transparent and opaque shades.

Excellent transparency and brilliance.

Unsurpassed resistance to ageing.

High surface hardness.

Scratch resistance.

Good recyclability.

High optical quality.

Glass-clear appearance.

Good outdoor performance.

Meets all current European food contact legislation and can be used in contact with foodstuffs.

APPLICATIONS

Automotive.

Building.

Lighting.

Food.

Signs.

Electrical.

Sanitary.

Marine.

Medical.

General Information
Features	Amorphous Food Contact Acceptable Good Weather Resistance High Clarity High Hardness High Scratch Resistance Opticals Outstanding Surface Finish Recyclable Material
Uses	Automotive Applications Building Materials Construction Applications Electrical/Electronic Applications Lighting Applications Marine Applications Medical/Healthcare Applications Non-specific Food Applications Sanitary Products
Agency Ratings	EU Food Contact, Unspecified Rating
Appearance	Clear/Transparent Colors Available Opaque
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Apparent Density	0.67	g/cm³	DIN 53466
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	11.0	cm³/10min	ISO 1133
Molding Shrinkage	0.30 to 0.50	%
Water Absorption (Equilibrium, 23°C, 50% RH)	0.30	%

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 961/30)	186	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3100	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Tensile Strain (Break)	3.0	%	ISO 527-2
Flexural Stress	105	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Water Vapor Permeability	0.90	g/m²/24 hr	DIN 53122

Thermal	Nominal Value	Unit	Test Method
Maximum Service Temperature - short cycle operation	80	°C

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.0	kJ/m²	ISO 179/1e
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	80.0	°C	ISO 75-2/Af
Vicat Softening Temperature	90.0	°C	ISO 306/B50
CLTE - Flow (23 to 80°C)	7.0E-5	cm/cm/°C	DIN 53752
Specific Heat	1500	J/kg/°C	IEC 1006
Thermal Conductivity	0.18	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Electric Strength ¹	60	kV/mm	IEC 60243-1
Dielectric Constant			IEC 60250
100 Hz	3.20
1 MHz	2.90
Dissipation Factor			IEC 60250
100 Hz	0.040
1 MHz	0.030
Comparative Tracking Index (Solution B)	600	V	IEC 60112

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.492		ISO 489
Transmittance (3000 µm)	92.0	%	DIN 5036-3
Haze	< 1.0	%	DIN 5036-3

Injection	Nominal Value	Unit
Processing (Melt) Temp	200 to 240	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	K20/P50

Resin Grade	Manufacturer	Category	Trademark
RTP 1405 TFE 15	RTP Company	PESU	RTP
Sylvin 8200-90 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Sylvin 86017-50 Red 6238	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Axiall PVC 1801 Clear 7002	Axiall Corporation	PVC, Flexible	Axiall PVC
PERLER® O07U1000B11	A.D. Compound S.p.A.	PP Copolymer	PERLER®