ULTEM™ CRS5111 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | If0cL0_ULTEMCRS5111resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5 VA listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 6.9 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4760 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 117 | MPa | ASTM D638 |
| Fracture | 112 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 4900 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 360 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 216 | °C | ASTM D648 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 343 - 366 | °C | |
| Middle Temperature | 354 - 377 | °C | |
| Front Temperature | 366 - 388 | °C | |
| Nozzle Temperature | 360 - 382 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 CR10 BK111 | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Vipel® F086-HHH-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| ADENE NFJA | A.D. Compound spa | PP Homopolymer | ADENE |
| LNP™ LUBRICOMP™ EFL36XXC compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| POLYfill PP TOUCH 34725 | Polykemi AB | PP, Unspecified | POLYfill |