INELEC PEICF20
| Category: | PEI , Polyether Imide |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IcPOD5_INELEC-PEICF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Specific Volume | 0.741 | cm³/g | |
| Molding Shrinkage - Flow | 0.15 to 0.25 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 195 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 213 | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 360 to 379 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vandar® 2122 | Celanese Corporation | PBT | Vandar® |
| Daelim Po1y® TR-480BL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Di-Pak™ E-4501 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Karina BLACK PVC COMPOUND TR-55-48/1 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF006S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |