| PP COPOLYMER, 10% TALCUM, UV STABILIZED, BLACK |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| 0°C | 14 | kJ/m² | ISO 180 |
| 23°C | 40 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 54.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 - 260 | °C | |
| Middle Temperature | 210 - 260 | °C | |
| Front Temperature | 210 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 4008 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Sumitomo Silicone SI 9045C | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| NPC PE HD-5502GA | NPC Alliance Corporation | HDPE | NPC PE |
| Generic Acetal (POM) Homopolymer - Glass Fiber | Generic | Acetal (POM) Homopolymer | Generic |
| TABOREN® PH 89 T 20-075 | SILON s.r.o. | PP Homopolymer | TABOREN® |