Shinko-Lac® ASA E510
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IVpInH_Shinko-Lac-ASA-E510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Shinko-Lac® ASA E510 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in North America for extrusion. Primary attribute of Shinko-Lac® ASA E510: Impact Resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 0.80 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 38.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 1910 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 58.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS8607A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Titacon® EX210 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| ALAMID® 6.6 S NATUR-9142 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| CHEMIGUM® P8D | Omnova Solutions Inc. | NBR | CHEMIGUM® |
| Kazan LDPE 15313-003 OKP 22 1111 2001 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |