Crastin® CE2054 BK580
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I8ltFW_CrastinCE2054BK580.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Polybutylene Terephthalate |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.9 | % | ISO 294-4 |
| Flow | 1.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.4 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 183 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 65.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| FMVSS Flammability | B | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 250 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Ejection Temperature | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 30 - 130 | °C | |
| Holding Pressure | 60.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solef® 31508 | Solvay Specialty Polymers | PVDF | Solef® |
| Eastar™ EN058, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| DynaStat® 1857 | Polymer Dynamix | Acetal (POM) Copolymer | DynaStat® |
| Karina IVORY PVC COMPOUND -E 75900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| VisiJet® FTX Cast | 3D Systems | Unspecified | VisiJet® |