Pro-fax EP349U
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hb2Sh0_Pro-fax-EP349U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax EP349U high flow polypropylene impact copolymer is available in pellet form. This resin is typically used in thin-wall injection molding applications and offers very good low temperature impact resistance. For regulatory compliance information see Pro-fax EP349U Product Stewardship Bulletin (PSB) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 1070 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BB3X | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Abstron TG3M | Bhansali Engineering Polymers Limited | ABS | Abstron |
| NYCOA Polyamide 471 R | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| DAPCO™ 3041FR | Cytec Industries Inc. | Epoxy | DAPCO™ |
| ORIENTENE RF 03 | Oriental Petrochemical Company | PP Homopolymer | ORIENTENE |