SPECIALTY PPA COMPOUND
PPA, 30% GLASS FIBER REINFORCED, HEAT STABILIZED, FOR THE HIGHEST TEMPERATURE APPLICATIONS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.70 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.20 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12500 | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 190 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.1 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.5 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 6.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 50 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.5 | -- | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 265 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 21 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CABELEC® CA6141 | Cabot Corporation | PC | CABELEC® |
| Braskem PE PLURIS4301 | Braskem | LLDPE | Braskem PE |
| GELOY™ HRA222F resin | SABIC Innovative Plastics Europe | ASA+PC | GELOY™ |
| Kumho SBR 1723L | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Sylvin 8200-85UV Clear 8447 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |