LEXAN™ 123SRM resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HL5h4B_LEXAN-123SRM-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flow, uv stabilised, impact modified, super release grade polycarbonate. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 140 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 97.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 124 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 134 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 71.0 to 93.0 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torayca® XTLP1040 | Toray Resin Company | Nylon 6 | Torayca® |
| WELLAMID Nylon 6000 GS 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| NuSil CV-2942 | NuSil Technology | Silicone | NuSil |
| LNP™ LUBRICOMP™ RX05050 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| LinGen FR280 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | LinGen |