VENELENE® FB-3030
| Category: | LDPE+LLDPE , Low Density Polyethylene + LLDPE |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HdVQk8_VENELENE-FB-3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.37 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Film Puncture Force (100 µm) | 12.7 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 100 µm | 23.0 | MPa | ASTM D882 |
| TD : Break, 100 µm | 21.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 100 µm | 400 | % | ASTM D882 |
| TD : Break, 100 µm | 700 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 100 µm | 180 | g | ASTM D1922 |
| TD : 100 µm | 450 | g | ASTM D1922 |
| Impact Resistance, Film | 280 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 70.0 | MPa | ASTM D882 |
| TD | 100 | MPa | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (100 µm) | 66.0 | % | ASTM D1003 |
| Haze (100 µm) | 32 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up ratio (BUR): 2 - 3. Die gap: 0.7 -1.2 mm. Height of cooling line: 4 -5 times Die gap Diameter. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hanwha Total PP BI518 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| ESTACARB 1601 OPALE | Cossa Polimeri S.r.l. | PC | ESTACARB |
| Kynar Superflex® 2500-25 | Arkema | PVDF | Kynar Superflex® |
| Sylvin 8773-60D Red 6240 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| LNP™ LUBRICOMP™ QFP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |