DIAMALOY ABSPC 750
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ABSPC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HIFwqp_DIAMALOY-ABSPC-750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAMALOY ABSPC 750 is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/3.8 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 61.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 4.5 | % | ASTM D638 |
| Flexural Modulus 4 | 2590 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 87.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 113 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 82.2 to 98.9 | °C | |
| Drying Time - Desiccant Dryer | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 204 to 227 | °C | |
| Middle Temperature | 204 to 238 | °C | |
| Front Temperature | 216 to 249 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Method I (3 point load), 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP332K | PolyMirae | PP Copolymer | Moplen |
| ABSCOM® FT3450 | Polymer Compounders Limited | ABS | ABSCOM® |
| Formolene® E924F | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| VALOX™ PDR7904 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| Wanthane® WHT-1180EC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |