SEPAZ™ CON E1366
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGwqMU_SEPAZ-CON-E1366.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ CON E1366 is a CF 30% reinforced PA66 product. SEPAZ CON E1366 has good properties with excellent mechanical properties and 10³ ohm/sq surface electric resistivity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 | % | ASTM D955 |
| Transverse flow | 0.25 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 255 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3 | 17800 | MPa | ASTM D790 |
| Flexural Strength 4 | 333 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | °C | ASTM D648 |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C |
| Injection instructions |
|---|
| Injection Speed: 40 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^ F20 FR6 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Tecodur® PB70 GR50 BK009 MX01 | Eurotec Engineering Plastics | PBT+PET | Tecodur® |
| Zytel® FG70G50HSLA BK309 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Geon™ Vinyl Flexible R148CE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina IVORY COMP (SP31497) -E 654N35/ 1-Y-EXT-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |