Generic Nylon 6 - Glass\Mineral
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGNG1C_Generic-Nylon-6---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 - 1.49 | g/cm³ | ASTM D792 |
| 23°C | 1.33 - 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 0.62 | % | ASTM D955 |
| 23°C | 0.39 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.70 - 1.0 | % | ASTM D570 |
| Saturated, 23°C | 1.5 - 6.6 | % | ASTM D570 |
| Saturated, 23°C | 5.4 - 7.0 | % | ISO 62 |
| Equilibrium, 23°C | 1.6 - 1.7 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 - 2.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 105 - 122 | ASTM D785 | |
| Ball Indentation Hardness | 189 - 213 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7490 - 8300 | MPa | ASTM D638 |
| 23°C | 5650 - 10100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 92.0 - 150 | MPa | ASTM D638 |
| Yield, 23°C | 74.4 - 127 | MPa | ISO 527-2 |
| Fracture, 23°C | 99.0 - 132 | MPa | ASTM D638 |
| Fracture, 23°C | 82.8 - 132 | MPa | ISO 527-2 |
| 23°C | 96.8 - 137 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 2.0 - 3.1 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 4.1 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6130 - 8420 | MPa | ASTM D790 |
| 23°C | 3400 - 12300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 124 - 221 | MPa | ASTM D790 |
| 23°C | 145 - 201 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 43 - 70 | J/m | ASTM D256 |
| 23°C | 3.8 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 4.9 - 41 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 - 216 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 198 - 216 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 188 - 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 178 - 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 95.0 - 180 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 220 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 216 - 220 | °C | |
| -- | 220 | °C | DSC, ISO 3146 |
| -- | 218 - 222 | °C | ISO 11357-3 |
| -- | 218 - 220 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 1.5E-5 - 3.1E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.9E-5 - 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.0E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+13 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 3.5 - 16 | kV/mm | ASTM D149 |
| 23°C | 16 - 36 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C) | 5.3E-3 - 0.020 | IEC 60250 | |
| Comparative Tracking Index | 400 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 952 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.2 - 90.9 | °C | |
| Drying Time | 2.9 - 5.2 | hr | |
| Suggested Max Moisture | 0.083 - 0.25 | % | |
| Suggested Shot Size | 55 | % | |
| Rear Temperature | 234 - 285 | °C | |
| Middle Temperature | 244 - 282 | °C | |
| Front Temperature | 255 - 285 | °C | |
| Nozzle Temperature | 245 - 285 | °C | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 79.1 - 101 | °C | |
| Injection Pressure | 6.89 - 89.6 | MPa | |
| Holding Pressure | 50.0 - 75.0 | MPa | |
| Back Pressure | 0.163 - 0.528 | MPa | |
| Screw Speed | 45 - 90 | rpm | |
| Cushion | 4.76 - 4.84 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 LF TFE 15 | RTP Company | PEEK | RTP |
| RTP 802 GB 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Elastollan® 1185A50V | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Petrotene® PP A3 G40 HF CNZ0207 PH356 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Moplen RP225N | LyondellBasell Industries | PP Random Copolymer | Moplen |