SABIC® HDPE PCGF0863
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gyd0cO_SABICHDPEPCGF0863.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCGF0863 resin is a high density homopolymer with good barrier properties. The grade offers high stiffness, high temperature resistance and relatively high grease resistance. The resin has a low gel level. Application SABIC® HDPE PCGF0863 is typically used for flexible packaging, pharmaceuticals and devices and release liners. Compliance to regulations SABIC® HDPE PCGF0863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.964 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, cast film | 580 | MPa | ISO 527-3 |
| TD : 25 µm, cast film | 580 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, cast film | 26.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, cast film | 24.0 | MPa | ISO 527-3 |
| MD : Fracture, 25 µm, cast film | 22.0 | MPa | ISO 527-3 |
| TD : Fracture, 25 µm, cast film | 18.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 25 µm, cast film | 700 | % | ISO 527-3 |
| TD : Fracture, 25 µm, cast film | 800 | % | ISO 527-3 |
| Oxygen Permeability 1(23°C, 25 µm, Cast Film) | 0.100 | cm³/m²/24 hr | Internal method |
| Water Vapor Transmission Rate (38°C, 100% RH, 25 µm, Cast Film) | 4.0 | g/m²/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 134 | °C | DIN 53765 |
| Enthalpy Change | 224 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 0% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide PX08000 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| UNIGARD™ HP HFDA-1544 NT | The Dow Chemical Company | PE Copolymer | UNIGARD™ |
| Gallonprene® GP320-75 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Later 4 G/30-V0CT2 | LATI S.p.A. | PBT | Later |
| MAJORIS FFR020X | AD majoris | PP, Unspecified | MAJORIS |