LNP™ LUBRICOMP™ JCL36E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGrkzs_LNP-LUBRICOMP-JCL36E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound JCL-4036 Product reorder name: JCL36E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.55 | g/cm³ | |
| -- | 1.54 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.010 to 0.030 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 26900 | MPa | ASTM D638 |
| -- | 26300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 142 | MPa | ASTM D638 |
| Yield | 145 | MPa | ISO 527-2/5 |
| Break 3 | 142 | MPa | ASTM D638 |
| Break | 145 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.59 | % | ASTM D638 |
| Yield | 0.57 | % | ISO 527-2/5 |
| Break 5 | 0.59 | % | ASTM D638 |
| Break | 0.58 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 23400 | MPa | ASTM D790 |
| -- 7 | 22900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 213 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 199 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 198 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.34 | ||
| vs. Itself - Static | 0.36 | ||
| Wear Factor - Washer | 25.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 10 | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 320 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 5.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 279 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 280 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 270 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 270 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6001-70A | RTP Company | TPE | RTP |
| Zhongfa PBT G-20V | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PBT | Zhongfa |
| Nanjing Hongrui PA66 A333 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Jackdaw PP ER36BK6546 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| LONGLITE® PBT 1100-205S | CCP Group | PBT | LONGLITE® PBT |