Baytec® RTC-092A
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GtNm8B_Baytec-RTC-092A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec RTC-092A is a two-component, 100%-solid rotational casting system with a Shore hardness of 92A. The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the polyol component is a polyether polyol blend. Baytec RTC-092A is a fast reacting system designed to be cast on rotating roll cores using the rotational casting technique. The system is typically used on rollers for the paper, textile, and steel industries and belt rollers. It can be pigmented to almost any color. As with any product, use of the Baytec RTC-092A system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 | |
| Hardness- Pusey & Jones | 20.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Deflection | ASTM D575 | ||
| 10% | 4.10 | MPa | ASTM D575 |
| 25% | 6.58 | MPa | ASTM D575 |
| 5% | 2.65 | MPa | ASTM D575 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 155 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 71.8 | kN/m | ASTM D624 |
| Cracking | 23 | kN/m | ASTM D1938 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 110, mixing ratio by capacity: 1.0 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 1.0 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Light yellow liquid Specific Gravity @ 25°C: 1.09 Viscosity @25°C: 2500 mPa Flash Point, PMCC: 216°C NCO: 9.8 wt% Part B Type: Polyol Appearance: White to amber liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 1500 mPa-s Flash Point, PMCC: 179°C Hydroxyl Number: 130 mg KOH/g Reactivity: Gel Time: 15 sec Tack Free: 1 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 95610 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PP |
| Telcar® TL-4145A | Teknor Apex Company | TPE | Telcar® |
| NYCOA Polyamide 2276 | Nycoa (Nylon Corporation of America) | Nylon Copolymer | NYCOA Polyamide |
| FLEXCHEM™ 8053 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Hostalen PP H1022 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |