Vyncolit® G920
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GrRsAw_Vyncolit-G920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit G920 is a glass fibre filled phenolic moulding compound with high mechanical and good thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.35 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Post Shrinkage | 0.15 | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.4 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Type | PF 2 C3 | ||
| Pourability | Good |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.60 | % | ISO 527-2 |
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Compressive Stress | 260 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 3.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VP-2 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Capilene® SW 75 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Kynar Flex® 2850 WR | Arkema | PVDF | Kynar Flex® |
| INTEGRAL™ 602 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| LNP™ LUBRICOMP™ ICL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |