LEXAN™ FXM121R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GqOb6u_LEXANFXM121Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC in special effects colors. Metallic and pearlescent additives. Color package may affect performance. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Outdoor Suitability | f2 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2340 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 61.0 | MPa | ASTM D638 |
| Fracture | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.2 | % | ASTM D638 |
| Fracture | 90 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2380 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 48.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.711 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 260 - 282 | °C | |
| Middle Temperature | 271 - 293 | °C | |
| Front Temperature | 282 - 304 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk 80R | Shanghai Niuk New Plastic Technology Co., Ltd. | PS (HIPS) | Niuk |
| Daicel PP PB6N3 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Karina BLACK PVC COMPOUND 90901-48/1-D-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LINATHENE® LL110 | USI Corporation | LLDPE | LINATHENE® |
| OXNILON 6 ST 33GF | Oxford Polymers | Nylon 6 | OXNILON 6 |