LightSpan® LS-6140

Category:	Silicone , Silicone
Manufacturer:	NuSil Technology
Trademark:	LightSpan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Go76Xa_LightSpan-LS-6140.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
From LEDs to fiber optics, NuSil Technology's LightSpan™ brand product line delivers the most comprehensive line of refractive index matching adhesives, encapsulants and thermosets available. The benefits of silicone include the following: Thermal Stability Low Ionic Species Maintain Optical Clarity (90% minimum @ 400nm) Low Moisture Absorption (<0.4%) Optimization for UV Resistance Adjustable Cure Low Outgassing Low Shrinkage, <1% Low Modulus: Stress reduction for bonding materials with different coefficients of thermal expansion Gernal Purpose: Optical Adhesives and Elastomers Comments: Low Volitility, non-phenyl containing

Message

From LEDs to fiber optics, NuSil Technology's LightSpan™ brand product line delivers the most comprehensive line of refractive index matching adhesives, encapsulants and thermosets available.

The benefits of silicone include the following:

Thermal Stability

Low Ionic Species

Maintain Optical Clarity (90% minimum @ 400nm)

Low Moisture Absorption (<0.4%)

Optimization for UV Resistance

Adjustable Cure

Low Outgassing

Low Shrinkage, <1%

Low Modulus: Stress reduction for bonding materials with different coefficients of thermal expansion

Gernal Purpose: Optical Adhesives and Elastomers

Comments: Low Volitility, non-phenyl containing

General Information
Features	Good Thermal Stability Good UV Resistance Low Moisture Absorption Low Shrinkage Low to No Outgassing
Uses	Adhesives
Processing Method	Encapsulating

Thermal	Nominal Value	Unit
CLTE - Flow	4.0E-4	cm/cm/°C

Optical	Nominal Value
Refractive Index	1.400

Thermoset	Nominal Value	Unit
Thermoset Components
Part A	Mix Ratio by Weight: 1.0
Part B	Mix Ratio by Weight: 1.0

Uncured Properties	Nominal Value	Unit
Viscosity
-- ¹	2.6	Pa·s
-- ²	3.7	Pa·s
Curing Time (150°C)	0.25	hr
Pot Life	180	min

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	50
Tensile Strength	5.86	MPa
Tensile Elongation at Break	90	%

Note Message
1 .	Part B
2 .	Part A

Resin Grade	Manufacturer	Category	Trademark
SCHULASINT™ F5400	ICO Polymers EMEA, A Division of A. Schulman	PP Random Copolymer	SCHULASINT™
Braskem PE STS7006	Braskem America Inc.	LDPE	Braskem PE
Generic PBT - Glass\Mineral	Generic	PBT	Generic
K-Flex EL 37 FR	Technovinyl Polymers India Ltd.	PVC Elastomer	K-Flex
Karina CLEAR PVC COMPOUND 65/200	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina