| Category: | PC+Styrenic , Polycarbonate + Styrenic |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-X |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Trwkzo_Novalloy-X-X72S2-Type-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-X X72S2 (Type W) is a polycarbonate styrene (PC styrene) material,. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-X X72S2 (Type W) are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 50 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 48.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 83.0 | °C | ISO 75-2/A |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 35.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| SatinFlo™ 90 | Vi-Chem Corporation | PVC, Flexible | SatinFlo™ |
| Shin-Etsu RTV KE-1204B | Shin-Etsu Silicones of America | Silicone Rubber, RTV-2 | Shin-Etsu RTV |
| Nypol® PA A3 BRC0215 NR449 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Starex VE-0856 U | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |