Generic HDPE Copolymer
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GkscIA_Generic-HDPE-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.951 - 0.954 | g/cm³ | ASTM D792 |
| 23°C | 0.953 - 0.959 | g/cm³ | ISO 1183 |
| -- | 0.944 - 0.956 | g/cm³ | ASTM D1505 |
| -- | 0.944 - 0.952 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.050 - 7.0 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.050 - 30 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 1.00 - 5000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 59 - 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 240 - 1210 | MPa | ASTM D638 |
| 23°C | 1000 - 1110 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 19.9 - 28.5 | MPa | ASTM D638 |
| Yield, 23°C | 25.9 - 26.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 13.0 - 38.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 7.3 - 13 | % | ASTM D638 |
| Fracture, 23°C | 96 - 1000 | % | ASTM D638 |
| Fracture, 23°C | 200 - 350 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 740 - 1310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 - 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 61.5 - 74.3 | °C | ASTM D648 |
| Brittleness Temperature | -118 - -73.8 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 - 128 | °C | ASTM D1525 |
| Peak Melting Temperature | 127 - 133 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 205 - 225 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPE CopolymerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 5008-2 | BCC Products Inc. | Epoxy | BCC Resins |
| Hostaform® C 9021 GV1/20 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Lucent PP TPP-130 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |
| TOTAL Polypropylene PPH 3272 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Thermec N™ 4314CF30 | Technical Polymers, LLC | PPA | Thermec N™ |