CERTENE™ EDF-226A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GhgXxm_CERTENE-EDF-226A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EDF-226A is a certified prime grade 6% ETHYLENE VINYL ACETATE (EVA) copolymer often used in the production of specialty films needing excellent heat sealability and impact strength. EDF-226A applications include freezer film, produce bags and films requiring good clarity. EDF-226A contains No slip and No antiblock. A melt temperature of 400°F or less is recommended to reduce the risk of polymer decomposition. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 28.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 350 | % | ASTM D882 |
| TD : Fracture, 38 µm | 650 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 140 | g | ASTM D1922 |
| TD : 38 µm | 100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 102 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (38.0 µm) | 2.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.5 mils (38 µm) film; blow-up-ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 204 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 TFE 13 | RTP Company | Nylon 66 | RTP |
| New-prene™ 7175B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Bynel® 41E871 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| ELASTOSIL® RT 685 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Rotuba CAB B9004 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |