Generic Acetal (POM) Copolymer - Glass Fiber
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgH4dn_Generic-Acetal-POM-Copolymer---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.43 - 1.65 | g/cm³ | ASTM D792 |
| 23°C | 1.45 - 1.65 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 2.6 - 19 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 3.0 - 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.29 - 6.23 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.27 - 1.2 | % | ASTM D955 |
| Transverse flow : 23°C | 0.98 - 2.1 | % | ASTM D955 |
| 23°C | 0.37 - 1.8 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.095 - 0.90 | % | ASTM D570 |
| 23°C, 24 hr | 0.090 - 0.70 | % | ISO 62 |
| Saturated, 23°C | 0.20 - 0.80 | % | ASTM D570 |
| Saturated, 23°C | 0.19 - 0.90 | % | ISO 62 |
| Equilibrium, 23°C | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 - 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 79 - 113 | ASTM D785 | |
| Ball Indentation Hardness | 179 - 230 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4360 - 11100 | MPa | ASTM D638 |
| 23°C | 2930 - 10600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 56.8 - 149 | MPa | ASTM D638 |
| Yield, 23°C | 59.5 - 131 | MPa | ISO 527-2 |
| Fracture, 23°C | 54.5 - 117 | MPa | ASTM D638 |
| Fracture, 23°C | 59.4 - 132 | MPa | ISO 527-2 |
| 23°C | 61.7 - 129 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.4 - 4.1 | % | ASTM D638 |
| Yield, 23°C | 2.1 - 2.3 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 7.4 | % | ASTM D638 |
| Fracture, 23°C | 1.3 - 4.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3040 - 9520 | MPa | ASTM D790 |
| 23°C | 2000 - 10100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 89.3 - 201 | MPa | ASTM D790 |
| 23°C | 89.1 - 177 | MPa | ISO 178 |
| Yield, 23°C | 69.0 - 276 | MPa | ASTM D790 |
| Coefficient of Friction | 0.14 - 0.60 | ASTM D1894 | |
| Wear Factor | 32 - 10000 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.4 - 9.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 36 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 40 - 82 | J/m | ASTM D256 |
| 23°C | 3.7 - 7.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 420 - 610 | J/m | ASTM D256 |
| 23°C | 18 - 43 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 5.60 - 10.4 | J | ASTM D3763 |
| 23°C | 1.00 - 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 166 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 161 - 165 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 155 - 165 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 158 - 162 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 149 - 160 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 165 - 166 | °C | ASTM D3418 |
| -- | 165 - 167 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.3E-5 - 6.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.9E-5 - 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.9E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 2.0E+3 - 1.3E+16 | ohms | ASTM D257 |
| -- | 1.0E+4 - 1.1E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 4.0E+3 - 2.5E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 2.5E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 18 - 32 | kV/mm | ASTM D149 |
| 23°C | 19 - 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.70 - 3.71 | ASTM D150 | |
| 23°C | 4.00 - 4.20 | IEC 60250 | |
| 23°C | 4.20 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 6.0E-3 - 6.1E-3 | ASTM D150 | |
| 23°C | 2.9E-3 - 9.5E-3 | IEC 60250 | |
| Comparative Tracking Index | 598 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 122 | °C | |
| Drying Time | 1.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.15 | % | |
| Suggested Max Regrind | 18 | % | |
| Hopper Temperature | 25.0 - 42.5 | °C | |
| Rear Temperature | 174 - 210 | °C | |
| Middle Temperature | 185 - 201 | °C | |
| Front Temperature | 185 - 216 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 79.9 - 107 | °C | |
| Injection Pressure | 83.2 - 95.7 | MPa | |
| Holding Pressure | 55.0 - 115 | MPa | |
| Back Pressure | 0.250 - 0.568 | MPa | |
| Screw Speed | 45 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 206H | RTP Company | Nylon 66 | RTP |
| Moplen EP2X30F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| Trademark PE mLLD1918C | Trademark Plastics Corporation | mLLDPE | Trademark PE |
| HiFill® HDPE TM40 | Techmer Engineered Solutions | HDPE | HiFill® |
| Sylvin 83039-74 White 1493 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |