Generic MAH-g
| Category: | MAH-g , Maleic Anhydride Grafted Polymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wBU4XU_Generic-MAH-g.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic MAH-g This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.875 - 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.50 - 12 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 1.3 - 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 21 - 98 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 8.00 - 16.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 - 1000 | % | ASTM D638 |
| Flexural Modulus (23°C) | 13.8 - 940 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 40.0 - 130 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 62.8 - 131 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenogel® ABS A3 FR NTLA010 AB314 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| XYRON™ L543V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| ALCUDIA® HDPE TR-156 | REPSOL | HDPE | ALCUDIA® HDPE |
| Five Plus™ CPP40C | Noble Polymers | PP Copolymer | Five Plus™ |
| Karina BLACK PVC COMPOUND -E 828-48/ 27-Y-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |