Pearlbond™ 125H
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GY3gRV_Pearlbond-125H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlbond® 125/H is polyester-based thermoplastic polyurethane, supplied in form of colourless, translucent granules, combining hardness with excellent low-temperature flexibility and a low softening point. Pearlbond® 125/H can be used for making heat-sealable fabrics (thermobonding), obtained by coating processes such as scattering or dot-coating (powder or paste). In all cases, the product is previously ground into powder, by cryogenic grinding. The particle size of the powder will depend on the application technique to be used. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| 20°C | 1.19 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 35 to 55 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| -- | 18.0 | MPa | |
| 100% Strain | 4.00 | MPa | |
| 300% Strain | 7.00 | MPa | |
| Tensile Strain (Break) | 520 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 4.00 | MPa | |
| 300% Strain | 7.00 | MPa | |
| Tensile Strength | 18.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 520 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 to 140 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 1(160°C) | 890 | Pa·s | ISO 1133 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Range | 110 to 130 | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.16 Kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 10712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Mytex® TSP-4023US | Mytex Polymers | PP, Unspecified | Mytex® |
| Hybrid B2026I | Ravago Manufacturing Americas, LLC | PC+PBT | Hybrid |
| Hostacom TRC 787N E1 G71535 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ LUX7432C resin | SABIC Innovative Plastics | PC | LEXAN™ |