SCHULADUR® A GF 30 HR2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GV3mkh_SCHULADURAGF30HR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced, hydrolysis stabilized PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 7000 | MPa | ISO 178 |
| Flexural Stress 2(4.0% strain) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 65 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 70 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210G35 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Borealis PE MG9641 | Borealis AG | HDPE | Borealis PE |
| LEXAN™ BM5225Y resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| ACRYREX® CM-205I | CHI MEI CORPORATION | Acrylic (PMMA) | ACRYREX® |
| POCAN® C 3230 XF 000000 | LANXESS GmbH | PC+PBT | POCAN® |